Polishing Pastes
.jpg)
OSKAR`S М-100 is a universal, fast-acting polishing paste for achieving a very good surface with a high gloss. Excellent cleaner for varnished, plastic and metal surfaces. Does not contain wax and silicone and is therefore recommended formachine polishing. Contains medium and small fractions of aluminum oxide, reduced content of emulsion, oil products and water.
Application
Apply with a clean cloth 40x50cm and polish until smooth. When using the clipper, do not exceed 2100 rpm. It is recommended to change rags frequently during work.
Specifications
| Index | Value |
| Form | Soft doughy paste |
| Color | White-gray |
| Smell | Specific |
| Specific gravity, g / ml | ≈ 1,3 |
| PH value | ≈ 8,0 |
| Grain size, μm | > 1 – 90 |
| Average grain size, μm | ≈ 10 |
| Solubility | Partially soluble in hydrocarbons |
Storage: Store in a cool and dry place, protected from frost. In original packaging for 24 months.
OSKAR’S M-50 POLISHING PASTE
OSKAR`S M-50 is a strong, fast-acting polishing paste for removing roughness and scratches from dies and finished parts. It is free of wax and silicone and is therefore recommended for high temperature and high pressure machine polishing. Contains coarse fractions of aluminum oxide, reduced emulsion content, oil products and water.
Application
Apply with a clean cloth 40x50cm and polish until smooth. When using the clipper, do not exceed 2100 rpm. It is recommended to change rags frequently during work.
Specifications
| Index |
Value |
| Form | Soft doughy paste |
| Color | White-gray |
| Smell | Specific |
| Specific gravity, g / ml | ≈ 1,3 |
| PH value | ≈ 8,0 |
| Grain size, μm | > 40 – 90 |
| Average grain size, μm | ≈ 60 |
| Solubility | Partially soluble in hydrocarbons |
Storage: Store in a cool and dry place, protected from frost. In original packaging for 24 months.
POLISHING PASTE BF-50
High-performance polishing and abrasive compound BF-50 is a strong, fast-acting polishing paste for removing roughness and scratches from dies and finished products. Free of wax and silicone and therefore recommended for high temperature and high pressure machine polishing. Supplied in metal cans of 1 kg.
Application
Apply BF – 50 with a soft cloth to the surface of the product measuring 50×50 cm and polish mechanically (max 2100 rpm) until the traces of the skin and scratches disappear. Then the polishing is continued with BF – 100 paste until the required gloss is achieved. In the final stage of polishing, the BF – 150 is used both manually and mechanically. The use of BF – 150 guarantees the highest glossiness of the surface and creates an excellent base for the subsequent application of release wax. When the paste begins to dry it is necessary to release the pressure for optimum gloss.
POLISHING PASTE BF-100
.jpg)
BF-100 Polishing and Grinding Compound is a versatile, fast-acting polishing compound for achieving a very good high-quality surface gloss. Excellent cleaner for varnished, plastic and metal surfaces. Free of wax and silicone, ideal for machine polishing. Supplied in metal cans of 1 kg.
Pastes do not contain silicon for mechanical polishing of matrices and fiberglass products. To obtain a high gloss, polishing should be completed with BF – 150.
Application
Apply BF – 100 with a soft cloth to the surface of the item measuring 50×50 cm and polish mechanically (max 2100 rpm) until traces of the skin and scratches disappear. In the final stage of polishing, the BF – 150 is used both manually and mechanically. When the paste begins to dry it is necessary to release the pressure for optimum gloss.