Сonstruction resins
Polimal® 103 AWTP-1
Structural, orthophthalic, thixotropic, low styrene emission, pre-accelerated with color curing indicator, unsaturated polyester resin. This polyester resin is used for the production of fiberglass laminates by hand and spray.
Polimal® 104 AWTP
Structural accelerated thixotropic orthophthalic unsaturated polyester resin with color cure indicator and low styrene emission. This polyester resin is recommended for the production of laminates up to 5 mm thick. The resin meets the requirements of DIN 16946/1 type 1140.
Benefits:
- high wettability of glass material
- fast set of hardness
- good mechanical parameters,
- high temperature resistance (HDT) and bending resistance.
Polimal® 104 WTP U
Structural, orthophthalic, accelerated, thixotropic resin with color curing indicator and UV stabilizer. This polyester resin is characterized by high thermal resistance (HDT) and good wetting and impregnating properties of glass material.
Complies with DIN 16 946/2 type 1140.
Polimal® 1057 AWTP
Structural moderately elastic thixotropic accelerated unsaturated polyester resin based on DCPD with a colored indicator hole and low styrene emission. Possesses excellent mechanical and technological properties. This polyester resin exhibits very good waviness and fiber impregnation characteristics.
Polimal® 1059 AWTP-1
Structural, moderately elastic, thixotropic, accelerated unsaturated DCPD based polyester resin with low styrene emission and color cure indicator. Possesses good mechanical and technological properties. This polyester resin exhibits very good wetting and fiber impregnation characteristics.
Polimal 1059 AWTP-1 approved by Lloyd’s Register.
Polimal® 1059 AWTP-2
Structural, moderately elastic, thixotropic, accelerated unsaturated DCPD based polyester resin with low styrene emission and color cure indicator. Possesses good mechanical and technological properties. This polyester resin exhibits very good wetting and fiber impregnation characteristics.
Polimal 1059 AWTP-2 approved by Lloyd’s Register.
Polimal® 1059 WTP-1
Constructional, moderately elastic, thixotropic, accelerated unsaturated polyester resin based on DCPD, with colored cure indicator. Possesses excellent mechanical and technological properties. This polyester resin exhibits very good wetting and fiber impregnation characteristics.
Polimal 1059 WTP-1 approved by Lloyd’s Register.
Polimal® 1094 AWTP-1
Structural, moderately elastic, orthophthalic, thixotropic, with low styrene emission, pre-accelerated with a colored indicator of curing, unsaturated polyester resin. This polyester resin is used for the production of fiberglass laminates up to 5 mm thick.
Polimal® 1094 AWTP-1 approved by Lloyd’s Reg.
Polimal® 1094 AWTP-2
Structural, moderately elastic, orthophthalic, thixotropic, with low styrene emission, pre-accelerated with a colored indicator of curing, unsaturated polyester resin. This polyester resin is used for the production of fiberglass laminates up to 5 mm thick.
Polimal® 1094 AWTP-1 approved by Lloyd’s Reg.
Polimal® 1094 AWTP-3
Constructional, moderately elastic, orthophthalic, thixotropic, with low styrene emission, pre-accelerated with a colored curing indicator, polyester unsaturated resin. This polyester resin is used for the production of fiberglass laminates with a thickness of more than 5 mm.
Polimal® 1094 AWTP-1 approved by Lloyd’s Reg.
Polimal® 1094 AWTP-1S
Structural, moderately elastic, orthophthalic, thixotropic, with low styrene emission, pre-accelerated with a colored indicator of curing, unsaturated polyester resin. This polyester resin contains a particulate white pigment which is titanium dioxide.
It is used for the production of fiberglass laminates up to 5 mm thick.
Polimal® 1094 AWTP-1 approved by Lloyd’s Reg.
Polimal® 1094 WTP-1
Structural, moderately elastic, thixotropic, pre-accelerated, with a colored indicator of hardening, orthophthalic unsaturated polyester resin. This polyester resin is used for the production of fiberglass laminates up to 5 mm thick.
Polimal 1094® WTP-1 approved by Lloyd’s Register.
Polimal® 143 AWTP-1
Structural accelerated thixotropic terephthalic unsaturated polyester resin with color cure indicator and low styrene emission. This polyester resin has a low viscosity and excellent strength properties.
Polimal® 143 AWTP-2
Accelerated, constructional, thixotropic, terephthalic unsaturated polyester resin with colored cure indicator and low styrene emission. This polyester resin has low viscosity and good strength parameters.
Polimal® 122-2 WTP
Structural accelerated thixotropic unsaturated polyester resin based on isophthalic acid with colored cure indicator. This polyester resin has excellent processing and mechanical properties. Possesses high temperature resistance and water resistance.
Polimal® 122-2 WTP-2
Structural, accelerated, thixotropic unsaturated polyester resin based on isophthalic acid, with colored cure indicator. It is characterized by excellent technological and mechanical parameters. This polyester resin is highly heat and water resistant.
Polimal® 1452 AWTP
This polyester resin is a structural, accelerated, terephthalic, unsaturated polyester resin with a colored cure indicator and reduced styrene emissions. It is characterized by excellent processing parameters.
Benefits:
- light impregnation of glass material
- low drainage from vertical surfaces.